In this study, the SCC behavior of X80 steel under SRB exposure, with and without cathodic polarization, is systematically evaluated. The results reveal that SRB accelerates the SCC … In this paper, the single and combined effect of sulfate-reducing bacteria (SRB) and cathodic potential on stress corrosion cracking (SCC) behavior of X70 pipeline steel in sea-mud... 此研究以“Micromechanisms of stress corrosion cracking induced by sulfate-reducing bacteria in a high-strength low-alloy steel”为题发表在《Acta Materialia》上,原文链 … A novel dual-functional material, lauryl betaine-lignin (LBL), was synthesized via Steglich esterification to inhibit sulfate-reducing bacteria (SRB)-induced corrosion, exploring the … Abstract Stress corrosion cracking (SCC) poses a severe threat to the long-term integrity of high-strength steel pipelines, particularly under complex environments involving cathodic …